Heterostructure with rear-face donor doping

ABSTRACT

The invention relates to a heterostructure with a buffer layer or substrate, a channel arranged on the buffer layer or substrate and a capping layer arranged on the channel. Said channel is made from a piezopolar material and either the region around the boundary interface between the buffer layer or substrate and the channel, or the region around the boundary interface between the channel and the capping layer is doped in such a way that any piezo charging which occurs at the respective boundary interface is compensated.

[0001] The present invention relates to a heterostructure as is for example applied in field effect transistors in power electronics and high temperature electronics. With this, in particular heterostructures which have an In(Ga)N channel, an (Al)GaN capping layer and a GaN buffer layer are used. On account of the material properties of GaN and their compounds such as AlGaN and InGaN these heterostructures have been intensively researched in order to permit applications in power electronics and high temperature electronics.

[0002] With heterostructures which have an In(Ga)N channel, an (Al)GaN capping layer and a GaN buffer layer or Ga substrate, the InGaN channel is stressed on account of the differing lattice constants. On account of the material, by way of this in the GaN/InGaN/GaN system there arise piezoelectric fields which at the boundary interfaces produce polarised charges (piezocharges). A GaN/InGaN/GaN heterostructure at the same time has a positive boundary interface charge at the InGaN/Ga transition and a negative boundary interface charge at the Ga/InGaN transition (interface). With an indium content of 100%, the produced boundary interface charges may reach a charge carrier density of 1.3×10¹⁴ cm⁻². The advantage of structure lies in the fact that the charges produced by the piezoelectric fields are located in the channel. On account of the material properties of GaN there additionally form spontaneous polarisation charges on the surface and on the buffer rear-face which however only have a secondary influence on the transistor properties.

[0003]FIG. 1 shows in its part picture 1A such a heterostructure with a buffer 1, with a channel 2, with a capping layer 3 and the boundary interfaces 5 and 6 between the layers 1/2 and the layers 2/3 respectively. Furthermore the piezocharges are shown, wherein one may recognise that the produced positive piezoecharge is located on the boundary interface 5 and the produced negative piezocharge is located on the boundary interface 6. The piezocharges then move oppositely according to the arrows A and B under the influence of an applied external field E.

[0004] From literature there are known modulation-doped (MODFET), channel-doped and undoped (piezo-FET) AlGaN/GaN field effect transistors. In the ALGaN/GaN system stresses also lead to piezoelectric fields which form polarised charges at the boundary interfaces. In contrast to a GaN/InGaN/GaN system both boundary interface charges are not located in the channel, but the negative charge at the AlGaN/GaN interface as 2DEG (2-dimensional electron gas) and the positive charge on the AlGaN surface.

[0005] The disadvantage of such a structure is the fact that the bonded boundary interface charge at the AlGaN/GaN boundary interface is in interaction with the counter-pole surface charge by way of the polarised fields. The surface charges in DC operation of a GaN-based transistor have little influence on the output characteristics. In RF operation the charge on the surface must follow the charnel charge on account of its interaction. Assuming the charges in the channel move at a higher speed the surface charge, then with a characteristic frequency in RF operation the surface charge no longer follows the chapel charge. This now counter-pole, quasi stationary charge violates the neutrality condition and may now trap the free charges in the channel with the result that the output current reduces and the maximal RF power reduces with respect to the DC power.

[0006] In contrast to the AlGaN/GaN system with the GaN/InGaN/GaN system no boundary interface charge produced by the piezoelectric polarisation is located on the sample surface. An interaction between the piezoelectric polarisation charge and the surface charge is avoided. By way of this the effect of current compensation and the resulting power reduction with a high-frequency entry power which is observed with AlGaN/GaN transistors is reduced.

[0007] In a GaN/InGaN/GaN the positive boundary interface charge on the rear-face In-GaN/GaN interface and the induced negative boundary interface charge on the GaN/InGaN front-face interface contribute to the transport of current. In comparison to GaN or AlGaN the electron movability in InGaN is considerably higher and according to theoretical computations may be 4500 cm²/Vsec. The movability of holes in the InGaN is however a multiple smaller than the electron movability. The resulting net current flow given by the positive boundary interface charge and negative boundary interface charge is determined by the condition of the charge neutrality, i.e. the slower hole current determines the resulting cut-off frequency of the component. Furthermore the channel may be blocked by a pn-transition.

[0008] It is then the object of the present invention to avoid the above mentioned disadvantages with heterostructures with a channel of a piezopolar material.

[0009] This object is achieved by the heterostructure according to patent claim 1 and the field effect transistor according to patent claim 24 as well as the use according to patent claim 28. Advantageous further formations of the heterostructure or field effect transistor are given in the respective dependent claims.

[0010] According to the invention for example by way of a thin n-doping in the channel or buffer or substrate the positive polarisation charge on the boundary interface between the buffer and channel is compensated so that there results only one electron channel. This is shown with reference to FIGS. 1B as well as 1C. 1B shows how, by way of the doping with a stationary donor 12, one may bring movable electrons 13 into the channel which recombine with the piezocharge 10 so that there merely remains the electrons 11 as movable charge carriers in the channel.

[0011]FIG. 1B shows the distribution of the charge on an inverted GaN/InGaN/GaN HEMT structure with donor-doping in the InGaN. FIG. 1C shows a farther possibility, specifically the distribution of the charge on an inverted Ga/InGaN/GaN HEMT structure with doner-doping in the buffer GaN. In a similar manner as in FIG. 1B one may clearly observe the compensation of the positive piezocharge 10 in the channel by the electron modulation doping from the doner layer 4 which is a doped region of the buffer 1. As a positive counter charge for the electron channel charge, after recombination of the charge 10 and 13 there merely remains a positive stationary doner charge 12 in the doped doner layer 4 of the buffer 1. FIGS. 2A and 2B show the simulated band course in a 20 nm GaN/20 nm InGaN/GaN buffer system, and the charge carrier distribution. For this simulation all layers are undoped and the indium content is 20%. In contrast FIGS. 3A and 3B show the simulated band course and the charge carrier distribution in a GaN/InGaN/GaN system with a N-compensation charge in the InGaN channel as in FIG. 1B. For this simulation a 10 nm thick N-compensation doping (1.5×10¹⁹ cm⁻³) is assumed in the InGaN channel.

[0012]FIG. 4a and FIG. 4B show a corresponding simulation of a system as in FIG. 1C, i.e. with a 10 nm thick N-compensation doping (1×10⁹ cm⁻³) as a doner layer in the GaN buffer below the channel. In both cases of FIGS. 3 and 4 the doping is chosen exactly such that the hole channel has been compensated.

[0013] From FIG. 3B and FIG. 4B and in comparison to FIG. 2B it may be directly recognised that the positive piezocharges on the boundary interface between the buffer and channel have been completely compensated and as a result a hole conduction is no longer present in the channel.

[0014]FIG. 5 shows the layer construction of an inverted Ga/InGaN/GaN field effect transistor with a rear-face donor doping according to the present invention. Here the doping was effected with silicon as a stationary donor (2×10¹⁸ cm³) in a 10 nm thick InGaN layer which lies at the boundary interface between the channel 2 and the buffer 1. The field effect transistor was deposited on a substrate of sapphire and additionally provided with contact electrodes 7, 8 and a gate electrode 9.

[0015] In indium content in the 10 nm undoped InGaN layer of the channel 2 and in the 10 nm thick doped InGaN:Si layer 4, 2 is approx 7%. The 3 μm thick buffer 1 and the 20 nm thick capping layer 3 are in each case undoped.

[0016]FIG. 6 shows the output characteristic line of this FET structure with 20 nm GaN undoped as a capping layer, 10 nm InGaN undoped as a channel, 10 nm InGaN doped (2×10¹⁸ cm⁻²) as a compensation layer with an indium content of 7% and a 3 μm thick GaN buffer layer which is likewise undoped. The gate length was selected at 0.5 μm. With this then a maximal saturation current of 250 mA/mm was achieved.

[0017] In the pinch condition with such a FET a breakdown voltage of 120 V was achieved. This resulted in an output power of 2.5 W/mm. In RF operation with an entry power of 16 dBm on a 50 Ohm load line up to 10 HZ one could ascertain no current compression. This represented in FIG. 7 which shows the maximal RF output current normalised to the maximum DC output current depending on the frequency with this FET of FIG. 5.

[0018]FIG. 8 shows the layer construction of an inverted InGaN-based BEMT with a rear-face doner-doping, which was likewise realised.

[0019] The doner doping of 1×10¹⁹ cm⁻³ is located in a 10 nm thick GaN layer 4 below the InGaN channel 2, separated from this by a 5 nm thick undoped INGaN spacer layer 21 for separating the doping rumps. The indium content in the 20 nm undoped InGaN layer 2 is 10%. The 3 μm thick GaN buffer 1 and the 20 nm thick GaN capping layer 3 are undoped. In FIGS. 9 and 10 the output characteristics of this structure are shown. With a transistor with 0.5 μm gate length (FIG. 9) and with a 0.25 μm gate length (FIG. 10) a maximum saturation current of 600 mA/mm and 900 mA/mm respectively was achieved.

[0020] With the previous examples which essentially correspond to FIGS. 1B and 1C it was shown that by way of the doner compensation doping of the free holes in an INGaN-based inverted HEMT structure there arises a free electron channel. It is however basically also possible to carry out an acceptor compensation doping of the free electrons and thus to produce a free hole channel. This permits complementary logic circuits to be constructed (analogous to CMOS circuit). In FIG. 11 there is shown the construction of such an invertor with an n-channel and a p-channel of InGaN-based HFET. At the same time for the same layers the same reference numerals have been used, wherein in the p-channel system the corresponding reference numerlas have been shown as apostrophied reference numerals (e.g. 3′ instead of 3 for the capping layer). The layer construction of the n-channel transistor at the same time corresponds to FIG. 8. The p-channel transistor consists of a 3 μm thick undoped GaN buffer 1 which in common ha the p-channel transistor with the p-channel transistor, of a 20 nm thick undoped InGaN layer 2′ with 10% indium as a channel, of a 5 nm thick magnesium-doped GaN layer for compensation doping of the electron chapel induced with this with an acceptor concentration of 2×10¹⁹ cm⁻³ as well as of a 20 nm thick undoped GaN capping layer 3′. In the n-type as well as the p-type transistor between the channel and the doped layer there is located a space layer 21 and 21′ respectively.

[0021] For compensating the two potentials of the a-type transistor or of the p-type transistor below the gate region of the two transistors an isolator 22, for example of SiO₂ or SIN is placed between the gates 9, 9′ and the semiconductor material of the capping layer 3, 3′.

[0022]FIG. 12 and FIG. 13 show the band course and the charge carrier distribution respectively of a p-channel InGaN-based heterostructure with n-compensation doping shown constructed as in the right part of the picture of FIG. 11. On applying a negative grain source voltage and a positive gate voltage one thus realises a p-channel transistor. This is shown in FIG. 14 in which the DT output characteristic line of such a p-channel HEFT with 0.5 μM gate length is shown. 

1. A heterostructure with a buffer layer or substrate, with a channel arranged on the buffer layer or on the substrate as well as with a capping layer arranged on the channel, wherein the channel consists of a piezopolar material, characterised in that either the region around the boundary interface between the buffer layer or substrate and channel or the region around the boundary interface between the channel and capping layer is doped in a manner such that the piezocharges occuring at the respective boundary interface are compensated. 